  Carbon burnt materials impregnated with metals and alloys

arbon-lead moulds of the grades
O-1500-C05; O-600-C05; -1500-05

Are used to manufacture the parts of friction blocks (liquid- and gastight at high pressures) operating in the conditions of dry, semi-dry and liquid friction upon steady or smoothly changing load.
For the parts made of the above said materials it is recommended to use cast iron, steel, chrome dressing as the countershank material; permissible specific pressure is 25-35 kgc/cm2; permissible speed is 15 m/s.
Permissible working temperature upon exploitation of products made of the above materials in the oxidizing, reducing and neutral media is 300 C.
Amount of wear at permissible specific pressures and speeds in the conditions of dry friction in the air at the indoor temperature for 100 hours of operation is not more than 30 mkm.
Carbon-lead materials are recommended to be used upon liquid and semi-liquid friction on all the stated materials, and upon dry friction on cast iron.
Carbon-lead materials are not recommended for the operation with nonferrous metals and their alloys. The advisable surface roughness of the counterpart should be Ra 0.12, State Standart 2789-73.

Size of moulds, mm
Diameter Length
Rated Tolerance Rated Tolerance
-1500-05 60 4 170 30
72 5 170 30
120 6 170 30
145 8 170 30
-00-05 195 8 170 30
235 10 170 30
-1500-05 60 4 170 30

Phisico-mechanical properties
Properties -1500-05 600-C05 -1500-05
Permissible specific load, kgc/cm2, max. 40 40 40
Permissible working speed,
m/s, max.
15 15 15
Permissible working temperature, C, max. 300 300 300

Note. Intensive heat elimination is necessary upon exploitation of the said grades of materials in the mode of dry friction. The friction coefficient of the above materials is within the scope of 0.7 to 0.15 in case of operation in the mode of dry friction